Author Affiliations
Abstract
1 Editorial Department, Ludong University, Yantai 264025,China
2 School of Physics and Optoelectronic Engineering, Ludong University, Yantai 264025, China
3 College of Physics and Engineering, Qufu Normal University, Qufu 273165, China
ZnO/diamond-like carbon (DLC) thin films are deposited by pulsed laser deposition (PLD), and the room-temperature photoluminescence (PL) is investigated. Using a fluorescence spectrophotometer, we obtain the PL spectra of DLC/Si and ZnO/Si thin films deposited at different substrate temperatures. The ZnO/DLC thin films show a broadband emission almost containing the entire visible spectrum. The Gaussian fitting curves of PL spectra reveal that the visible emission of ZnO/DLC thin films consists of three peaks centered at 381 nm, 526 nm and 682 nm, which are attributed to the radiative recombination of ZnO and DLC, respectively. The Commission International de l,Eclairage (CIE) 1931 (x, y) chromaticity space of ZnO/DLC thin films indicates that the visible PL spectrum is very close to the standard white-light region.
光电子快报（英文版）
2012, 8(6): 445
1 鲁东大学 物理与光电工程学院, 烟台 264025
2 鲁东大学 学报编辑部, 烟台 264025
为了获取高质量、高取向排列规则的ZnO纳米棒, 玻璃衬底预先用脉冲激光沉积方法制备一层ZnO薄膜作为籽晶层, 应用水热法在玻璃衬底上生长ZnO纳米棒。探究了籽晶层及不同溶液浓度对ZnO纳米棒结构和发光的影响, 用扫描电子显微镜和X射线衍射仪测量样品的形貌和结构, 用组建的光致发光测试系统对样品的室温光致发光光谱进行测定。结果表明, ZnO纳米棒具有高度取向且分布致密均匀; 光致发光光谱显示ZnO的近带边发射比深能级发光略低; 随着溶液浓度的增加, 近带边发光和深能级发光相对强度的比值依次降低。
薄膜 光致发光 水热法 脉冲激光沉积 ZnO纳米棒 thin films photoluminescence hydrothermal method pulsed laser deposition ZnO nanorods
1 鲁东大学学报编辑部，山东 烟台 264025
2 鲁东大学物理与光电工程学院， 山东 烟台 264025
3 曲阜师范大学物理工程学院，山东 曲阜 273165
在从室温到800 ℃的温度范围内，用脉冲激光沉积方法在Al2 O3 (0001)衬底上制备了ZnO薄膜。采用X射线衍射仪、 原子力显微镜以及荧光光谱仪分别研究了衬底温度对ZnO薄膜表面形貌、结晶质量和光致发光特性的影响。X射线衍射仪和原子力显微镜的结果表明，当衬 底温度从室温升高到400 ℃时，ZnO薄膜的结构及结晶质量逐渐提高，而当衬底温度超过400 ℃时，其结构和结晶质量变差；在400 ℃下生长 的ZnO薄膜具有最佳的表面形貌和结晶质量。室温光致发光的测量结果表明，400 ℃下生长的ZnO薄膜的紫外发光强度最强，且发光波长最短(386 nm)。
ZnO薄膜 激光脉冲沉积 衬底温度 光致发光 ZnO thin film PLD substrate temperature photoluminescence